SP 1 | SP 2 | SP 3 | SP 4 | SP 5 | Mean | Fashions comparison | |
---|---|---|---|---|---|---|---|
Total separation (mm) | P = 0.008 | ||||||
Figure-of-eight | 0.41 | 0.31 | 0.29 | 0.30 | 0.29 | 0.32 | |
Figure-of-zero | 0.28 | 0.20 | 0.17 | 0.17 | 0.15 | 0.19 | |
Pressure (MPa) | P = 0.666 | ||||||
Figure-of-eight | − 0.10 | + 0.06 | + 0.23 | + 0.28 | + 0.40 | + 0.17 | |
Figure-of-zero | − 0.05 | + 0.12 | + 0.26 | + 0.36 | + 0.48 | + 0.23 | |
IPSA% | P = 0.617 | ||||||
Figure-of-eight | 40.00 | 42.87 | 30.27 | 20.43 | 13.98 | 29.51 | |
Figure-of-zero | 36.82 | 37.43 | 27.62 | 14.86 | 10.46 | 25.44 | |
Stress of K-wires (MPa)* | P = 0.625 | ||||||
Figure-of-eight | 142.51 | 110.88 | 96.64 | 92.73 | 85.13 | 105.58 | |
Figure-of-zero | 141.49 | 104.56 | 86.46 | 82.68 | 72.54 | 97.55 | |
Stress of SS-wires (MPa)* | P = 0.096 | ||||||
Figure-of-eight | 95.01 | 76.62 | 84.58 | 89.46 | 92.40 | 87.61 | |
Figure-of-zero | 85.80 | 74.33 | 80.58 | 79.08 | 82.78 | 80.51 |